Lidhjet e nikelit TIG ERNiCrFe-7A Lidhje saldimi
![未标题-1](http://www.welding-honest.com/uploads/未标题-123.jpg)
![fd1](http://www.welding-honest.com/uploads/fd1.jpg)
![未标题-2](http://www.welding-honest.com/uploads/未标题-222.jpg)
KOMPONETI KIMIK:
aliazh (wt%) | C | Mn | Si | Cr | Ni | Mo | Fe | Nb+Ta | P | S |
RREGULLAT GB/T | - | - | - | - | - | - | - | - | - | - |
RREGULLAT AWS | 0.04 | 1.00 | 0.50 | 28,0-31,5 | Rem | 0.50 | 7,0-11,0 | 0,5-1,0 | 0.02 | 0,015 |
VLERA SHEMBULL | 0,028 | 0.15 | 0.11 | 29.8 | 59.03 | 0.06 | 9.8 | 0,86 | 0.001 | 0,002 |
VETITË MEKANIKE:
PRONËSIA | FUQIA E RENDIMIT (MPa) | FORCËSIA E ZGJATIMIT (MPa) | VLERA E NDIKIMIT J/℃ | ZGJATIMI (%) | Trajtimi termik | ||||||
RREGULLAT GB/T | - | - | - | - | - | ||||||
RREGULLAT AWS | - | - | - | - | - | ||||||
VLERA SHEMBULL | - | 760 | 133/Temperatura e dhomës | 37 | 607°C*25h |
![03](http://www.welding-honest.com/uploads/0360.jpg)
Teli saldimi me gaz aliazh nikel-krom-hekur me bazë nikel, përbërja nominale është 60%Ni-29%Cr-9%Fe-0,75%Nb.
Karakteristikat e mira mekanike të metalit të shkrirë, veçanërisht rezistenca ndaj plasaritjes së ulët plastike (DDC).
![02](http://www.welding-honest.com/uploads/0274.jpg)
![01](http://www.welding-honest.com/uploads/0188.jpg)
Përmbajtja e lartë e Cr e bën atë të ketë rezistencë të shkëlqyer ndaj korrozionit të stresit ndaj plasaritjes në mjedisin me ujë të pastër në kushte rrezatimi. Hark i qëndrueshëm, formim i bukur, rrjedhje e mirë e hekurit të shkrirë, me performancë të shkëlqyer të procesit të saldimit.
![未标题-8](http://www.welding-honest.com/uploads/未标题-82.jpg)
![未标题-7](http://www.welding-honest.com/uploads/未标题-72.jpg)
![03](http://www.welding-honest.com/uploads/0340.jpg)
![04](http://www.welding-honest.com/uploads/0424.jpg)
![b0780de687c3deca16d616279ad5fd6](http://www.welding-honest.com/uploads/b0780de687c3deca16d616279ad5fd6.png)
![08](http://www.welding-honest.com/uploads/087.jpg)
![05](http://www.welding-honest.com/uploads/0518.jpg)
![07](http://www.welding-honest.com/uploads/0711.jpg)
![06](http://www.welding-honest.com/uploads/0614.jpg)
![01](http://www.welding-honest.com/uploads/0196.jpg)
![02](http://www.welding-honest.com/uploads/0282.jpg)
![03](http://www.welding-honest.com/uploads/0368.jpg)
-
Projekti i impiantit qendror të trajtimit të Xinjiang Kela 2
-
Material saldimi për silenciator
![577445SDA01](http://www.welding-honest.com/uploads/577445SDA01.jpg)
KOMPONETI KIMIK:
aliazh (wt%) | C | Mn | Si | Cr | Ni | Mo | Fe | Nb+Ta | P | S |
RREGULLAT GB/T | - | - | - | - | - | - | - | - | - | - |
RREGULLAT AWS | 0.04 | 1.00 | 0.50 | 28,0-31,5 | Rem | 0.50 | 7,0-11,0 | 0,5-1,0 | 0.02 | 0,015 |
VLERA SHEMBULL | 0,028 | 0.15 | 0.11 | 29.8 | 59.03 | 0.06 | 9.8 | 0,86 | 0.001 | 0,002 |
VETITË MEKANIKE:
PRONËSIA | FUQIA E RENDIMIT (MPa) | FORCËSIA E ZGJATIMIT (MPa) | VLERA E NDIKIMIT J/℃ | ZGJATIMI (%) | Trajtimi termik | ||||||
RREGULLAT GB/T | - | - | - | - | - | ||||||
RREGULLAT AWS | - | - | - | - | - | ||||||
VLERA SHEMBULL | - | 760 | 133/Temperatura e dhomës | 37 | 607°C*25h |
Shkruani mesazhin tuaj këtu dhe na dërgoni